Resin-SZUV-S9006-high tenacity
Introduction of 3D Printing Materials
Characteristics
SZUV-S9006 ???
PRODUCT DESCRIPTION?
SZUV-S9006?is an ABS like SL resin which has high-toughness?features. It is designed for solid state SLA printers.?SZUV-S9006?can be applied in master patterns, concept models, assembly parts and functional prototypes in the?field of automotive, medical and consumer electronics industries. The parts durability building with SZUV-S9006?is over 6.5months.
TYPICAL FEATURES
-Liquid resin's medium viscosity, so easy recoating, easy to clean parts and machines?
-Improved strength retained, improved dimensions retention of parts in humid condition?
-need minimal part finishing
-Long shelf life in machine
-Low bottom contraction?
?
TYPICAL BENEFITS
-Need less part finishing time, easier post-curing?
-Bulid accurate and high tough parts with an improved dimensional stability?
-High quality controls for vacuum casting parts
-Low shrink and good resistance to yellowing?
-Magnificent white color?
-Outstanding machinable SLA material??
Note: the temperature of szuv-s9006 should not be too high. Please use it below 25℃. The relative humidity for use and storage must be under 38RH%.
Application Cases
SOME OF MY PROJECTS
Education
Hand Molds
Auto Parts
Packaging Design
Art Design
Medical
?Physical Properties (Liquid)?
| Appearance | White |
| Density | 1.11-~1.15g/cm3?@ 25 ℃ |
| Viscosity | 230~290cps @ 26?℃ |
| Dp | 0.13~0.145?mm |
| Ec | 9.5~10.5?mJ/cm2 |
| Building layer thickness | 0.05~0.12mm |
?
Mechanical Properties (Post-Cured)?
| MEASUREMENT? | TEST METHOD? | VALUE |
| 90-minute UV post-cure | ||
| Hardness, Shore D | ASTM D 2240 | 75-85 |
| Flexural modulus, Mpa | ASTM D 790 | 2,592-2,675 |
| Flexural strength, Mpa | ASTM D 790 | 63-70 |
| Tensile modulus, MPa | ASTM D 638 | 2,489-2,595 |
| Tensile strength, MPa | ASTM D?638 | 36-53 |
| Elongation at break | ASTM D 638 | 15-25% |
| Poisson’s Ratio | ASTM D 638 | 0.4-0.44 |
| Impact strength notched Izod, J/m | ASTM D 256 | 45-70 |
| Heat deflection temperature, ℃ | ASTM D 648 @66PSI | 38-50 |
| Glass transition,Tg | DMA，E”peak | 40-54 |
| Coefficient of thermal expension | TMA(T<Tg) | 90~102*E-6 |
| Density, g/cm3 | ? | 1.12-1.18 |
| Dielectric Constant60 Hz | ASTM D 150-98 | 4.2-5.0 |
| Dielectric Constant?1 kHz | ASTM D 150-98 | 3.3-4.2 |
| Dielectric Constant1 MHz | ASTM D 150-98 | 3.2-4.0 |
| Dielectric?StrengthkV/mm | ASTM D 1549-97a | 12.8-16.1 |
?